Xylitol; Expanded graphite; Shape-stable; Supercooling; Long-term thermal energy storage
资金
- National Natural Science Foundation of China [52036008]
The study demonstrates that xylitol/expanded graphite composite PCMs have potential in long-term thermal energy storage, with the thermal conductivity of the composite PCM increasing significantly by adding expanded graphite content, although it reduces the latent heat. Different performances were observed during the charging and discharging process of the composites.
Xylitol with high latent heat of 243.28 kJ/kg and a significant supercooling degree has been considered to be a potential phase change material (PCM) for long-term thermal energy storage (TES). Xylitol can be kept in a supercooled or supersaturated metastable for a long time. In our study, it took 23 days and 30 min respectively that xylitol liquid and xylitol liquid adding 5 wt% ethanol crystallized completely at room temperature of 15 +/- 5 degrees C. Unfortunately, the low thermal conductivity and leakage of xylitol restrict its thermal performance. In this paper, xylitol/expanded graphite (EG) composite PCMs with 5, 8, 10, 12 and 15 wt% EG content were prepared by an impregnation and compression two-step method. The results of SEM, XRD and FT-IR show that xylitol is well impregnated into the micropores of EG and has good chemical compatibility. The thermal performance test shows that the thermal conductivity of composite PCMs increases dramatically and the latent heat decreases with the increase of EG. The experimental results show that the latent heat of 10 wt% EG is 209.73 kJ/kg and 192.18 kJ/kg, respectively, during the charging and discharging process. The thermal conductivity of 10 wt% EG is 3.91 W/(m.K), as 9.29 times as xylitol. Besides, the crystallization of xylitol in EG and the mass loss of the composites have also been studied. The results show that 10 wt% EG composites crystallized completely after 16 days. These results prove that xylitol/EG composite PCMs have broad application prospects in long-term TES.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据