Weak Electron Irradiation Suppresses the Anomalous Magnetization of N-Doped Diamond Crystals

出版社

WILEY-V C H VERLAG GMBH
DOI: 10.1002/pssb.202100395

关键词

color centers; diamond; magnetism

资金

  1. DFG [DFG-ES 86/29-1, DFGME 1564/11-1]
  2. Russian Foundation for Basic Research (RFBR)
  3. National Natural Science Foundation of China (NSFC) [20-52-53051]
  4. Projekt DEAL

向作者/读者索取更多资源

The experiment showed that the presence of magnetic C centers in nitrogen-doped diamond crystals is responsible for the large hysteresis behavior observed, and reducing the concentration of these centers can completely suppress the phenomenon. Additionally, partial recovery of the hysteresis behavior was observed after annealing the samples at high temperatures in vacuum.
Several diamond bulk crystals with a concentration of electrically neutral single substitutional nitrogen atoms of less than or similar to 80 ppm, the so-called C or P1 centers, are irradiated with electrons at 10 MeV energy and low fluence. The results show a complete suppression of the irreversible behavior in field and temperature of the magnetization below 30 K, after a decrease in less than or similar to 40 ppm in the concentration of C centers produced by the electron irradiation. This result indicates that magnetic C centers are at the origin of the large hysteretic behavior found recently in nitrogen-doped diamond crystals. This is remarkable because of the relatively low density of C centers, stressing the extraordinary role of the C centers in triggering those phenomena in diamond at relatively high temperatures. After annealing the samples at high temperatures in vacuum, the hysteretic behavior is partially recovered.