Synthesis and characterization of polycrystalline Mo2BC ceramic

期刊

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 41, 期 10, 页码 5109-5114

出版社

ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2021.04.041

关键词

Mo2BC ceramic; Microstructure; Mechanical properties; Transmission electron microscopy

资金

  1. National Natural Science Foundation of China [51805513, U1804252]
  2. Key Scientific Research Project Fund of Education of Henan Province, China [20A430009]
  3. Foundation of State Key Laboratory of Solid Lubrication, China [LSL-2014]

向作者/读者索取更多资源

Single-phase polycrystalline Mo2BC ceramic bulks were successfully synthesized using spark plasma sintering method at a low synthesis temperature of 1300 degrees C. The ceramic exhibited high Vickers hardness and typical brittle features, with intergranular and transgranular fractures as the main failure modes.
Single-phase polycrystalline Mo2BC ceramic bulks were synthesized successfully from molybdenum, boron, and graphite powders using the spark plasma sintering method. Herein, it was established that the synthesis temperature of the Mo2BC ceramic could be as low as 1300 degrees C. Transmission electron microscopy (TEM) characterization confirmed that the crystal structure of the Mo2BC ceramic was comparable to that of the MoAlB ceramic. The Vickers hardness of the Mo2BC ceramic was measured to be 18.1 GPa. Additionally, the compressive strength, flexural strength, and fracture toughness were determined to be 1.74 GPa, 457.72 MPa, and 3.26 MPa. m1/2, respectively. The Mo2BC bulk exhibited typical brittle features, in which intergranular and transgranular fractures were the main failure modes.