Nanoindentation studies of strain rate sensitivity in bulk metallic glasses

Nanoindentation tests were conducted on Pd40Cu30Ni10P20, [(Fe0.6Co0.4)(0.75)B0.2Si0.05](96)Nb-4, Zr48Cu34Pd2Al8Ag8 and Zr48Cu32Ni4Al8Ag8 bulk metallic glasses to determine their strain rate sensitivities of hardness. Strain rate sensitivities for different experimental conditions were calculated, it was found that all specimens exhibit negative strain rate sensitivity. Different variation trend of strain rate sensitivity values along with different factors were observed, these observations were utilized to discuss the reasons for negative strain rate sensitivity, and its dependence on the composition and other factors of metallic glasses.

Automated summary

Nanoindentation tests were conducted on different bulk metallic glasses to determine their strain rate sensitivities of hardness, which were found to be negative. The variations in strain rate sensitivity values along with different factors were observed and discussed to understand the reasons for this negative strain rate sensitivity and its dependence on the composition and other factors of metallic glasses.