HP40Nb steel; Area fraction; Carbide; Life assessment; Image analysis
资金
- Chung-Ang University
- KOEN [2020-Hyunjang(Balun)-01]
Life assessment predictions were made for reformer tubes made of HP40Nb grade steel in the petrochemical industry, with correlations established between the area fractions of precipitated carbides and service periods. The study found that an increase in precipitate area fractions was directly proportional to service times, and this relationship could be utilized for on-site residual life assessments using the surface replication method.
Life assessment predictions of reformer tubes of HP40Nb grade steel used in the petrochemical industry were investigated by quantitative metallographic evaluations of the area fractions of precipitated carbides. Correlations were established between the field-service periods and area fractions of the carbides via microstructural analysis. The microstructures of the virgin and other tubes were examined using optical microscopy (OM) for service periods of 1.8, 6.0, 7.2, 8.5, 9.7, and 16.2 years at 950 degrees C. The area fractions of the precipitates were measured by image analysis using ImageJ software. The results showed that increase in the area fractions of the precipitates was almost proportional to increase their service times. The relationships between area fractions of the precipitates and service times were also discussed for a 6-year cracked tube and a tube that had been in service for 11.5 years at another furnace. The obtained relationship can thus be used via the surface replication method for on-site residual life assessments.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据