JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
卷 32, 期 13, 页码 17512-17523出版社
SPRINGER
DOI: 10.1007/s10854-021-06284-9
关键词
-
类别
资金
- Department of Science and Technology (DST), Government of India [CRG/2018/001426]
- DST
In this study, particulate composites of (1 - x)Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT)-xNi(0.8)Zn(0.2)Fe(2)O(4 )(NZFO) were prepared by the conventional solid-state method with x values of 0.2, 0.3, and 0.4. The composites exhibited mixed spinel-perovskite phases, and changes in dielectric properties, magnetic behavior, and magnetoelectric coupling were observed with variations in ferrite content. The highest magnetoelectric coupling coefficient was found in the x = 0.4 composite.
In this work, (1 - x)Ba0.85Ca0.15Zr0.1Ti0.9O3 (BCZT)-xNi(0.8)Zn(0.2)Fe(2)O(4 )(NZFO), where x = 0.2, 0.3, and 0.4, particulate composites were prepared by conventional solid-state method. X-ray diffraction (XRD) data confirmed that the composites exist in mixed spinel-perovskite phase for all compositions. Field emission scanning electron microscopy (FESEM) was used to calculate the grain size distribution and surface morphology. The composites were investigated for the relative dielectric constant with variation in temperature and frequency. Polarization (P) vs. electric field (E) loops of the composites appear to be lossy with the increase in ferrite content. Magnetic hysteresis (M-H) loops show the increase in saturation magnetization with an increase of ferrite content. Change in dielectric properties is studied under varying magnetic fields and observed maximum change in x = 0.4 composite. We observed maximum magnetoelectric coupling (ME) coefficient in x = 0.4 composite, i.e., 7.71 mV/cm Oe in unpoled and 9.45 mV/cm Oe in poled samples.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据