关键词
Wrought Mg-Bi alloys; Hot deformation; Twinning; Dynamic recrystallization; Dislocation slip; Texture
资金
- National Natural Science Foundation of China [51704209, 51701060, 51901153]
- Natural Science Foundation of Shanxi province [201801D121088, 201901D211096]
- Science and Technology Major Project of Shanxi Province [20191102007, 20191102008]
This study systematically investigated the twinning behavior, dynamic recrystallization (DRX) mechanism, and texture evolution of extruded Mg-xBi (x=0.5 wt.%, 2.0 wt.%) alloys during hot compression. The results show that the texture types and intensities are closely related to twinning behavior and DRX mechanism. The formation and variation of {10 (1) over bar2} extension twins dominate the early evolution of texture, while the DRX mechanism plays a greater role as the strain increases.
The twinning behavior, dynamic recrystallization (DRX) mechanism and the resultant texture evolution of the extruded Mg-xBi (x=0.5 wt.%, 2.0 wt.%) alloys were systematically investigated during hot compression at the strain rate of 10 s(-1) and temperature of 200 degrees C. The results indicate that the types and intensities of the texture are greatly dependent on the twining behavior and DRX mechanism. At the initial stage, the evolution of texture is mainly domination by the formation and variation of {10 (1) over bar2} extension twins, which is beneficial to the compression direction (CD) -tilted basal texture. With an increase in the strain, the texture evolution is more greatly regulated by the DRX mechanism. Besides, the pyramidal slip and basal slip are activated during the compression process, resulting in the Schmid factors (SF) of pyramidal slip remain at similar to 0.4 and the average SFs for basal slip increase from 0.2 to 0.34 as the strain increase. These findings provide a new insight into controlling the texture of wrought Mg-Bi-based alloys during hot deformation processing. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.