JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
卷 106, 期 -, 页码 98-107出版社
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/j.jmst.2021.08.012
关键词
Resistive switching; Ta2O5/ZrO2 bilayer film; Barrier layer thickness; Multilevel resistance states; RESET-stop voltage
资金
- National Research Foundation of Korea (NRF) - Korean government (MSIP) [2021R1C1C1004422]
- Dongguk University
- National Research Foundation of Korea (NRF) - Ministry of Science, ICT & Future Planning [NRF-2020M3F3A2A02082449, NRF-2016R1A6A1A03013422]
This study demonstrates that the optimization of the interfacial barrier layer can improve the switching cycle endurance and uniformity of resistive random access memory (ReRAM) devices. The results show that a Ta2O5 barrier layer with a thickness of approximately 2 nm provides lower forming voltage, narrow distribution of SET-voltages, good switching cycles, high pulse endurance, long retention time, and reliable multilevel resistance states. The multilevel resistance states were scientifically investigated by modulating the compliance current and RESET-stop voltages, and were found to be distinct and stable. The ZrO2-based ReRAM device with an optimized Ta2O5 barrier layer is a promising candidate for multilevel data storage memory applications.
The multilevel storage capability of nonvolatile resistive random access memory (ReRAM) is greatly desired to accomplish high functioning memory density. In this study, Ta2O5 thin film with different thicknesses (2, 4, and 6 nm) was exploited as an appropriate interfacial barrier layer for limiting the formation of the interfacial layer between the 10 nm thick sputtering deposited resistive switching (RS) layer and Ta ohmic electrode to improve the switching cycle endurance and uniformity. Results show that lower forming voltage, narrow distribution of SET-voltages, good dc switching cycles (10(3)), high pulse endurance (10(6) cycles), long retention time (10(4) s at room temperature and 100 degrees C), and reliable multilevel resistance states were obtained at an appropriate thickness of similar to 2 nm Ta2O5 interfacial barrier layer instead of without Ta2O5 and with similar to 4 nm, and similar to 6 nm Ta2O5 barrier layer, ZrO2-based memristive devices. Besides, multilevel resistance states have been scientifically investigated via modulating the compliance current (CC) and RESET-stop voltages, which displays that all of the resistance states were distinct and stayed stable without any considerable deprivation over 10(4) s retention time and 10(4) pulse endurance cycles. The I-V characteristics of RESET-stop voltage (from -1.7 to -2.3 V) of HRS are found to be a good linear fit with the Schottky equation. It can be seen that Schottky barrier height rises by increasing the stopvoltage during RESET-operation, resulting in enhancing the data storage memory window (on/off ratio). Moreover, RESET-voltage and CC control of HRS and LRS revealed the physical origin of the RS mechanism, which entails the formation and rupture of conducting nanofilaments. It is thoroughly investigated that proper optimization of the barrier layer at the ohmic interface and the switching layer is essential in memristive devices. These results demonstrate that the ZrO2-based memristive device with an optimized similar to 2 nm Ta2O5 barrier layer is a promising candidate for multilevel data storage memory applications. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.