Electroplating of Zn-Ni Alloy Coating on Mild Steel and Its Electrochemical Studies

期刊

出版社

SPRINGER
DOI: 10.1007/s11665-021-06051-1

关键词

antibacterial activity; brightener; corrosion; electrodeposition; throwing power; Zn-Ni alloy coating

向作者/读者索取更多资源

A new sulfate bath has been optimized for the deposition of Zn-Ni electroplating on mild steel, resulting in bright and uniform coatings with good corrosion resistance. The bath composition and operating conditions were optimized, and various coating properties were discussed, including Ni content, hardness, thickness, throwing power, and corrosion resistance. The corrosion performance was investigated using different methods, and the antibacterial activity of the extract was also evaluated.
A new sulfate bath having ZnSO4.6H(2)O, NiSO4.6H(2)O, citric acid, and methanol extract in combination was optimized for the deposition of Zn-Ni electroplating on mild steel. The bath composition and operating conditions were optimized by the Hull cell experiment. The effect of current density (CD), pH, and temperature on coating properties like Ni content, hardness, thickness, throwing power, and corrosion resistance was discussed. The corrosion performance has been investigated by potentiodynamic polarization and electrochemical impedance spectroscopy methods. The antibacterial activity of the extract was carried out by the agar diffusion method. The electroplating having about 1.51% of nickel content (at optimized current density 4 A dm(-2)) was found to be bright and uniform, showing good corrosion performance against corrosion, and shows the highest corrosion resistance (8.62 mu A cm(-2)) at optimized current density 4 A dm(-2). The microstructures of the deposits were examined with scanning electron microscopy (SEM). The nickel contents in the deposit were analyzed with colorimetric technique and cross-checked by energy-dispersive x-ray analysis (EDX). A novel sulfate bath for Zn-Ni alloy coating on mild steel has been proposed and results are discussed.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据