Al Alloy Tailor-Welded Blanks Fabrication via Friction Stir Welding: Effect of Shoulder Size

出版社

ASME
DOI: 10.1115/1.4052295

关键词

friction stir welding; Tailor-welded blanks; tool shoulder size; mechanical properties; thermal analysis; microhardness; microstructure; advanced materials and processing; sustainable manufacturing; welding and joining

向作者/读者索取更多资源

The size of the tool shoulder significantly affects the quality of joints in friction stir welding of tailor-welded blanks. Increasing the shoulder size leads to larger grain size, elimination of void defects, and the highest strength observed in joints fabricated with an 18 mm shoulder size.
Material flow and heat generation by tool shoulder during Friction Stir Welding (FSW) significantly alters the microstructural and thermomechanical behavior of joints. The effect of shoulder size on mechanical properties of joints has not yet been reported in the FSW of Tailor-Welded Blanks (TWBs). This article reports the effect of shoulder size on joint quality in FSW of TWBs between 6.35 mm thick plates of AA2024-T3 and 2.5 mm thick plates of AA7475-T7 alloys in butt joint configuration fabricated under shoulder sizes: 18 mm, 20 mm, and 22 mm. Microstructural evaluation of FSWed joints reveals a significant increase in grain size with shoulder size. The X-ray energy-dispersive spectroscopic (EDS) elemental maps reveal the presence of fine second phase particles in the stir zone. The progressive elimination of void defects with the increase in shoulder size was observed. The tensile testing reveals the highest strength of joints fabricated via shoulder size of 18 mm. Fractographic analyses of broken tensile specimens showed the mixed mode of failure in all the welded specimens.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据