期刊
JOURNAL OF HAZARDOUS MATERIALS
卷 424, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jhazmat.2021.127324
关键词
Corrosion scale; Heavy metals; Drinking water distribution system; Microanalysis; Pipe burst; Corrosion bacteria
This study analyzed deposits from damaged pipelines to investigate corrosion and corrosion products, revealing differences in chemical composition and microbial communities under different corrosion conditions. Additionally, significant correlations were found between certain heavy metals and specific bacterial communities, indicating potential risks to consumer health.
Microbial corrosion and heavy metal accumulation in metal water supply pipelines aggravate scale formation and may result in pipeline leakage or bursting events. To better understand the corrosion and corrosion products in the damaged pipes, deposits excavated from three damaged pipes after 22-26 year service periods were analyzed. Using a combination of advanced micro-mineral techniques and 16S rRNA high-throughput sequencing, the micromorphology, chemical composition, and bacterial community were investigated systematically. Unlined pipe wall scales ruptured while lined pipes leaked due to joint scales. Dendrogram correlation results demonstrated that V/As, Al/Pb, and Cr/Mn clusters exhibited co-adsorption and co-precipitation characteristics. FTIR and XRD analysis detected the presence of gamma-FeOOH, alpha-FeOOH in loose scales, and Fe3O4 in rigid scales. Scales were colonized by various corrosion bacteria, with sulfate reducing bacteria and ammonia producing bacteria being dominant in the scales of anticorrosive and non-corrosive pipe, respectively. Tl, Ca, Al, and Pb exhibited an extremely positive correlation with Rhodocyclaceae, Ferritrophicum, Thermodesulfovibrionia, and Clostridiaceae. Al and V presented a potential Hazard Quotient risk to consumers, while Cd was potentially bioavailable in all inner scales. Overall, this study provides valuable information for the effective management and avoidance of corrosion-induced pipeline damage and heavy metal release.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据