JOURNAL OF ENVIRONMENTAL SCIENCES
卷 107, 期 -, 页码 98-110出版社
SCIENCE PRESS
DOI: 10.1016/j.jes.2021.02.001
关键词
Lithium aluminum silicate glass-ceramics; NaOH; Lithium; Leaching
资金
- Technology Innovation Program - Ministry of Trade, Industry & Energy (MOTIE, Korea) [20003877]
The study investigated the behavior and mechanism of Li leaching from lithium aluminum silicate glass-ceramics using aqueous NaOH solution. The efficiency of Li leaching was found to increase with higher NaOH concentration, specific surface area, and reaction temperature. However, prolonged leaching time may result in a decrease in Li leached due to the formation of zeolite around the glass-ceramics.
The behavior and mechanism of Li leaching from lithium aluminum silicate glass-ceramics which can be used as a secondary source of Li using aqueous NaOH solution was investigated. The Li leaching efficiency is increased with increasing concentration of NaOH, specific surface area, and reaction temperature. When leached under optimum conditions, 2 mol/L NaOH, 53 mu m particle undersize, 1:10 solid/liquid ratio, 250 r/min stirring speed, 100 degrees C reaction temperature, 12 hr, the Li leaching efficiency was approximately 70%. However, when the leaching experiment was performed for 48 hr, the concentration of Li+ ions contained in the leach liquor decreased from 1160 to 236 mg/L. To investigate the origin of this phenomenon, the obtained leach residue was analyzed by X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. These analyses show that zeolite was formed around the lithium aluminum silicate glass-ceramics, which affected the leaching of by adsorbing Li+ ions. In addition, using the shrinking-core model and the Arrhenius equation, the leaching reaction with NaOH was found to depends on the chemical reaction of the two reactants, with a higher than 41.84 kJ/mol of the activation energy. (c) 2021 The Research Center for Eco-Environmental Sciences, Chinese Academy of Sciences. Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据