corrosion; carbon steel; 1 M HCl solution; corrosion inhibitor; Schiff base
资金
- Liaoning Provincial Department of Education [lnjc202016, lnzd201905]
- Xingliao Talent Program of Liaoning Province [XLYC2002005]
The Schiff base N,N'-bis(4-hydroxy-benzylidene)-triethylenetetramine (N,N'-BHMTT) showed excellent performance as a corrosion inhibitor for carbon steel in 1 M HCl, with a corrosion inhibition efficiency of up to 82.5%. It slowed both cathodic and anodic corrosion processes of carbon steel, while forming a protective film that acted as a barrier against corrosive media effectively contacting the carbon steel surface.
To investigate the corrosion of carbon steel in acidic media, weight loss measurements, electrochemical methods, thermodynamic adsorption isotherms and scanning electron microscopy (SEM) observations were adopted to study the Schiff base N,N'-bis(4-hydroxy-benzylidene)-triethylenetetramine (N,N'-BHMTT) as a corrosion inhibitor for carbon steel in 1 M HCl. The corrosion inhibitor exhibited excellent performance. The corrosion inhibition efficiency was as high as 82.5% at 25 mg L-1 N,N'-BHMTT (weight loss result). The corrosion inhibitor simultaneously slowed the cathodic and anodic corrosion processes of carbon steel. N,N'-BHMTT is a mixed corrosion inhibitor with an almost unchanged corrosion potential. The adsorption of N,N'-BHMTT on the surface of carbon steel obeyed the Langmuir adsorption isotherm along with a mixture of physical and chemical adsorption, forming a complete and dense protective film on the carbon steel surface that acted as a barrier to inhibit corrosive media from effectively contacting the carbon steel surface.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据