Over-heating triggered thermal runaway behavior for lithium-ion battery with high nickel content in positive electrode

The thermal abuse of high specific energy NCM811 lithium-ion power battery in the process of use or safety test was simulated by winding resistance wire heating method, and local heating and uniform heating were carried out to trigger a thermal runaway. When thermal runaway triggered by uniform heating, the safety valve is opened timely and only open flame occurred without explosion, it did not cause the internal short circuit, and the safety valve was not damaged. However, when thermal runaway triggered by the local heating method, it caused a serious internal short circuit, the released electrolyte and other material burned violently and exploded, and the safety valve was completely damaged. In this process, a thin film heat flux sensor is also used to quantify the surface heat flux during thermal runaway, which could provide the test method and calculation basis for the thermal management design. The experimental results were also compared with those of NCM111, NCM 532 and NCM 622 batteries, the results revealed that increase of nickel content in positive electrode would also increase the degree of damage when a TR triggered by local heating method. (c) 2021 Elsevier Ltd. All rights reserved.

Automated summary

The experiment simulated thermal abuse of NCM811 battery using different heating methods, revealing that thermal runaway triggered by local heating caused more serious damage compared to uniform heating.