Moisture absorption characteristics and effects on mechanical properties of Kolon/epoxy composites

Para-aramid fibers (Kolon) are high performance polymeric fibers characterized by their high tenacity and impact resistance. They are used for the soft body armor structures in ballistics. In this study, the testing specimens were made from multilayered Kolon fabrics impregnated with epoxy resin where silicon carbide (SiC) microparticles or SiC nanofibers were added as reinforcement. The laminated composite samples were fabricated by hot compression and curing of epoxy resin. The tensile and impact strengths of the untreated specimens were compared with the ones that underwent water absorption in duration of 72 h (immersion or humidity) followed by desorption. The immersion of the specimens in water and exposure to high humidity (70%) were performed according to the ISO 62 standard while the tensile test was carried out in accordance with the ASTM D 3039 standard. In the end, the tensile test simulation of the laminated composite by using software Abaqus (R) was accomplished.

Automated summary

In this study, laminated composite samples made from para-aramid fibers were tested for water resistance by adding silicon carbide microparticles or nanofibers as reinforcement. The results showed that the composites maintained high tensile and impact strengths even after water absorption.