2205 DSS; 2507 DSS; chloride ion; micro-area electrochemical testing; pitting
资金
- Science and Technology Commission of Shanghai Municipality [19DZ2271100, 18DZ2204500]
- Natural Science Foundation of Shanghai [20ZR1421500]
The corrosion resistance of duplex stainless steel 2205 DSS and 2507 DSS decreased with increasing Cl- concentration in simulated flue gas condensate environment. Active sites appeared on the surface of 2205 DSS at a lower Cl- concentration compared to 2507 DSS, resulting in higher surface roughness and weight loss.2507 DSS exhibited lower degree of general corrosion and less surface corrosion products.
The corrosion behavior of duplex stainless steel 2205 DSS and 2507 DSS in simulated flue gas condensate of a waste incineration power plant at 180 degrees C was compared by micro-area electrochemical testing, surface and weight loss analysis. The results showed that the corrosion resistance of the two stainless steels decreased with the increase of Cl- concentration. After 48 h of corrosion, when the Cl- concentration was not less than 6 g.L-1, active sites where current density increased suddenly appeared on the surface of 2205 DSS, accompanied by the obvious increase of surface roughness and the weight loss. The lowest Cl- concentration that caused the appearance of active sites on the surface of 2507 DSS was 20 g.L-1, with less surface corrosion products and lower degree of general corrosion.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据