The study investigates the damage and failure of CFRP composites under isothermal mechanical loads in different thermal regimes, including ambient and cryogenic temperatures. Different types of materials and matrix systems are considered in the experimental study to analyze the applicability of standard composite failure criteria in the cryogenic regime.
The present study is concerned with damage and failure of CFRP composites under isothermal mechanical loads in the ambient and cryogenic thermal regimes. In an experimental study, the mechanical failure behavior of unidirectionally carbon fiber reinforced materials is investigated at ambient temperature and in a liquid Helium environment at 4.2 K under a variety of loading conditions. The effect of thermally induced damage is investigated on specimens exposed to cryogenic temperature without external mechanical load and subsequent testing till failure at ambient temperature. Three different materials including high modulus and intermediate modulus high strength fibers as well as epoxy and thermoplastic (PEEK) matrix systems are considered. The results are employed to investigate the applicability of different standard composite failure criteria in the cryogenic regime.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据