Ammoniated salt based solid sorption thermal batteries: A comparative study

Gas-solid chemisorption pairs of ammonia and halide salts have an edge over other pairs for advanced thermal energy storage batteries due to their abundance, easy availability, cost effectiveness, high sorption capacity, and wide operating temperature range. In the present work, thermodynamic analyses of thermal battery systems are performed for various ammonia-halide salt pairs using measured sorption characteristics. The stored thermal energy can also be upgraded by forming a combination of suitable halide salts. A maximum gravimetric energy storage density of 1664 kJ kg(-1) is observed for MnCl2 based thermal battery. The degree of heat upgradation can be as high as 43 degrees C in case of MnCl2-CaCl2 based resorption thermal battery. The first law efficiency is observed to be as high as 0.42 for CaCl2 based thermal battery. The decrease in first law efficiency due to parasitic mass is observed to be in the range of 26-37 % and 57-66% for different CaCl2 and MnCl2 thermal batteries, respectively. It is possible to recover the stored thermal energy in the form of simultaneous heating and cooling effects by using specific combination of salts which enhances the overall efficiency. First law efficiency as high as 0.92 can be achieved with a CaCl2-NaBr resorption thermal battery delivering simultaneous cooling and heating effects at 10 and 55 degrees C, respectively, while storing thermal energy at 100 degrees C.

Automated summary

Gas-solid chemisorption pairs of ammonia and halide salts are advantageous for advanced thermal energy storage batteries, providing high energy storage density and heat upgradation effects while reducing the first law efficiency. Specific combinations of salts can achieve simultaneous heating and cooling effects during thermal energy storage.