Block Copolymer Nanoparticles are Effective Dispersants for Micrometer-Sized Organic Crystalline Particles

Well-defined sterically stabilized diblock copolymer nanoparticles of 29 nm diameter are prepared by RAFT aqueous emulsion polymerization of methyl methacrylate using a dithiobenzoate-capped poly(glycerol monomethacrylate) precursor. These nanoparticles are evaluated as a dispersant for the preparation of organic crystalline microparticles via ball milling. This is exemplified for azoxystrobin, which is a broad-spectrum fungicide that is widely used to protect various food crops. Laser diffraction and optical microscopy studies indicate the formation of azoxystrobin microparticles of approximately 2 mu m diameter after ball milling for 10 min at 400 rpm. Nanoparticle adsorption at the surface of these azoxystrobin microparticles is confirmed by electron microscopy studies. The extent of nanoparticle adsorption on the azoxystrobin microparticles can be quantified using a supernatant assay based on solution densitometry. This technique indicates an adsorbed amount of approximately 5.5 mg m(-2), which is sufficient to significantly reduce the negative zeta potential exhibited by azoxystrobin. Moreover, this adsorbed amount appears to be essentially independent of the nature of the core-forming block, with similar data being obtained for both poly(methyl methacrylate)- and poly(2,2,2-trifluoroethyl methacrylate)-based nanoparticles. Finally, X-ray photoelectron spectroscopy studies confirm attenuation of the underlying N1s signal arising from the azoxystrobin microparticles by the former adsorbed nanoparticles, suggesting a fractional surface coverage of approximately 0.24. This value is consistent with a theoretical surface coverage of 0.25 calculated from the adsorption isotherm data. Overall, this study suggests that sterically stabilized diblock copolymer nanoparticles may offer a useful alternative approach to traditional soluble copolymer dispersants for the preparation of suspension concentrates affecting the context of agrochemical applications.

Automated summary

Well-defined sterically stabilized diblock copolymer nanoparticles of 29 nm diameter were prepared as a dispersant for organic crystalline microparticles. These nanoparticles effectively adsorbed onto the surface of azoxystrobin microparticles, reducing the negative zeta potential exhibited by azoxystrobin.