EUROPEAN POLYMER JOURNAL
卷 84, 期 -, 页码 421-434出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.eurpolymj.2016.09.051
关键词
Proton exchange membrane; Fuel cell; Polybenzimidazole; Composites; Hydrogen bonding
资金
- SERB, Govt. of India [SB/S1/PC-054/2013]
- UGC
In the present work, proton exchange membrane (PEM) based on series of polybenzimidazole (PBI) composites are prepared with acidic surfactant like molecules (ASMs) with an objective to improve properties of PEM especially proton conductivity. Composites are obtained by homogenizing poly (4, 4'-diphenylether-5, 5'-bibenzimjdazole) (OPBI) in three different ASMs namely camphorsulfonic acid (CSA), p-toluenesulfonic acid (PTSA) and mono-n-dodecyl phosphate (MDP). FT-IR and solid-state NMR studies indicate the presence of interactions between OPBI and ASMs which are necessary for obtaining homogeneous composite membranes. Mechanical reinforcement is observed in case of composite membranes and storage modulus increases with increasing ASM loading in the composite. The detailed thermal analysis shows that phosphoric acid loaded (PA) composite membranes have higher thermal stability than the PA loaded pristine OPBI, it increases with increasing loading of ASM and it largely depends upon the type of ASM in the composite. Though OPBI is an amorphous polymer but ASMs self-organizes themselves in the polymer matrix owing to the strong interaction between OPBI and ASMs. As a result composite membranes display the crystalline character which in turn significantly influences the morphological features of the composites. Fibrillar to porous morphology are observed in composites depending on the type and loading of ASM. This morphological features and the crystalline nature of the composites are found to be responsible for mechanical reinforcement and significant increase in PA loading. The PA doped pristine OPBI, OPBI/CSA-20%, OPBI/PTSA-20% and OPBI/MDP-20% composite membranes proton conductivities are 8.6 x 10(-2) S/cm, 2.82 x 10(-1) S/cm, 1.71 x 10(-1) S/cm and 1.43 x 10(-1) S/cm, respectively at 180 degrees C. OPBI/ASM composite membranes also display very low acid leaching in comparison to pristine OPBI owing to the formation of strong interaction between PA and polymer chains through ASMs. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据