One-Year Clinical Aging of Low Stress Bulk-Fill Flowable Composite in Class II Restorations: A Case Report and Literature Review

Bulk-fill flowable composites provide functional and aesthetic restorations while eliminating incremental composite layering and saving time. The degradation of the adhesive interface with subsequent gap formation is a concern when adhesively luted restorations are placed. Moreover, the number of adhesive interface failures increases when they are exposed to long-term water storage. The aim of the present study was to evaluate the morphological characteristics of the tooth-composite interface in class II cavities restored with a low stress bulk-fill flowable composite after aging in an oral environment. We describe a case of a patient with class II cavities in four premolars restored with a low stress bulk-fill flowable composite Surefil SDR (Dentsply DeTrey GmbH, Konstanz, Germany). The occlusal part was restored with nano-hybrid resin composite Ceram X Mono (Dentsply DeTrey GmbH). After one year of clinical function, the teeth were extracted and examined in a scanning electron microscope (SEM). It can be concluded that the application of bulk-fill covered with conventional composite seems to provide the homogeneous and stable bond to tooth structure after one year of aging in an oral environment. However, some defects within the dentin-resin composite interface were observed.

Automated summary

After restoring class II cavities in an oral environment with low stress bulk-fill flowable composite covered with conventional composite, a homogeneous and stable bond to tooth structure was observed after one year of aging. However, some defects within the dentin-resin composite interface were noted.