期刊
RESULTS IN PHYSICS
卷 24, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.rinp.2021.104117
关键词
Cu-Co nano ferrite; Cr-doped; XRD; FT-IR; Resistivity; VSM study
Complex ferrite nanoparticles were synthesized using sol-gel auto combustion technique. X-ray diffraction (XRD) analysis confirmed a single-phase cubic spinel structure with Fd-3m space group. The samples exhibited semiconductor properties with decreasing DC resistivity as temperature increased. Vibrating sample magnetometer (VSM) was used to characterize magnetic features.
Using sol-gel auto combustion technique complex ferrite nanoparticles have been synthesized. Characterization with the help of X-ray diffraction (XRD) revealed that the synthesized materials Cu0.7Co0.3Fe2-xCrxO4 are of a single-phase cubic spinel structure with Fd-3 m space group. And also, the samples' crystallite sizes calculated using XRD data yielded in the range of 19.28-32.92 nm. The lattice constants are calculated to be between 8.4099 angstrom and 8.4441 angstrom. The FTIR results revealed that the spinel structure remained undisturbed even after the Cr ions were doped. FESEM images display the materials constitute polygonal-shaped grains though at times irregularly shaped gains with slight agglomeration appear. EDS analysis confirmed that the sample contained the constituent elements. A decreasing pattern in DC resistivity with an increase in temperature was observed, ensuring the semiconducting character of the ferrites under investigation. VSM was utilized to characterize and estimate the magnetic features like magnetic saturation and coercivity of the samples.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据