Study of Diffusible Behavior of Hydrogen in First Generation Advanced High Strength Steels

期刊

METALS
卷 11, 期 5, 页码 -

出版社

MDPI
DOI: 10.3390/met11050782

关键词

diffusion coefficient; DP steel; CP steel; H concentration; trap density; activation energy

向作者/读者索取更多资源

The banded microstructure and higher C content in DP steels resulted in higher H diffusivity, while the higher fraction of H present in stronger traps in CP steels suggests better hydrogen embrittlement resistance. The non-uniform distribution of H in the specimens with higher concentration near the charging surface was also observed.
This study deals with microstructural influence on the H permeation behavior of Dual-Phase (DP) and Complex Phase (CP) steels using electrochemical permeation studies. The H diffusion coefficients in DP steels (DP800: 1.65 x 10(-10) m(2)center dot s(-1), DP1000: 1.58 x 10(-10) m(2)center dot s(-1)) are half of that found in CP steels (3.07 x 10(-10) m(2)center dot s(-1)).The banded microstructure along the specimen thickness and higher C content of the DP led to high H diffusivity of DP steels. The lower total H concentration along with a higher fraction of H was present in the stronger traps in CP steels suggest a better HE resistance of this steel. The H distribution in the specimens was non-uniform, with a higher H concentration speculated near the charging surface.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据