short fatigue crack; large scale yielding; low cycle fatigue; J-integral; austenitic stainless steel; residual lifetime prediction
资金
- Czech Science Foundation [19-25591Y]
Two approaches were tested to describe short fatigue crack growth under large-scale yielding conditions: the plastic component of the J-integral and the Polak model of crack propagation. It was found that the employed continuum mechanics models were able to give satisfactory results for stainless steels Sanicro 25 and 304L, despite their different properties. The residual fatigue lives estimated by these models were in good agreement with the experimental data, suggesting the potential of the plastic part of J-integral as a tool to model fatigue crack propagation.
In this work two approaches to the description of short fatigue crack growth rate under large-scale yielding condition were comprehensively tested: (i) plastic component of the J-integral and (ii) Polak model of crack propagation. The ability to predict residual fatigue life of bodies with short initial cracks was studied for stainless steels Sanicro 25 and 304L. Despite their coarse microstructure and very different cyclic stress-strain response, the employed continuum mechanics models were found to give satisfactory results. Finite element modeling was used to determine the J-integrals and to simulate the evolution of crack front shapes, which corresponded to the real cracks observed on the fracture surfaces of the specimens. Residual fatigue lives estimated by these models were in good agreement with the number of cycles to failure of individual test specimens strained at various total strain amplitudes. Moreover, the crack growth rates of both investigated materials fell onto the same curve that was previously obtained for other steels with different properties. Such a master curve was achieved using the plastic part of J-integral and it has the potential of being an advantageous tool to model the fatigue crack propagation under large-scale yielding regime without a need of any additional experimental data.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据