DOI: 10.3390/ma14081855
关键词
magnesium alloys; powder metallurgy; microstructure; mechanical properties; corrosion resistance
类别
资金
- Natural Science Foundation of Shandong Province [ZR2019QEE032]
- Shandong Higher Education Youth Innovation and Technology Support Program [2019KJB021]
The study found that increasing manganese content in Mg-Mn-Zn alloys improved their mechanical properties and corrosion resistance. Among the tested alloys, Mg-1.0Mn-2.0Zn showed the best performance and is more suitable for use in human body fluids.
The magnesium alloys Mg-0.5Mn-2Zn, Mg-1.0Mn-2Zn, and Mg-1.5Mn-2Zn (wt.%) with potential biomedical applications, synthesized by powder metallurgy, were investigated to evaluate the influence of manganese content on their microstructure, mechanical properties, and corrosion resistance. The results show that Mg-Mn-Zn alloys prepared by powder metallurgy reached the maximum compressive stress of 316 MPa and the maximum bending strength of 186 MPa, showing their good resistance to compression and bending, and meeting the mechanical properties required for the human bone plate. With an increase in manganese content, the corrosion resistance improved. In the polarization curve, the maximum positive shift of corrosion potential was 92 mV and the maximum decrease of corrosion current density was 10.2%. It was concluded that, of the alloys tested, Mg-1.0Mn-2.0Zn (wt.%) had the best overall performance, and its maximum compressive stress force and corrosion current density reached 232.42 MPa and 1.32 x 10(-5) A center dot cm(-2), respectively, being more suitable for service in human body fluids.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据