Fabrication of FeCoCrNiMnAl0.5-FeCoCrNiMnAl gradient HEA coating by laser cladding technique

In this study, an FeCoCrNiMnAl0.5-FeCoCrNiMnAl gradient high-entropy alloy (HEA) coating was fabricated by laser cladding. The gradient HEA coating was subjected to compression at 600 degrees C, and the phase structure, grain orientation, recrystallization state, grain boundary distribution, dislocation content and plastic deformation resistance of the coating were systematically studied by EBSD technology. The gradient HEA coating had a compression strength of 504 MPa with an elongation of 82% at 600 degrees C, and the surface of the FeCoCrNiMnAl cladding layer exhibited no obvious cracks. The gradient HEA coating exhibited an excellent balance between strength and toughness. The FeCoCrNiMnAl cladding layer formed a fiber texture parallel to the compression direction, and its body-centered cubic (BCC) structure had a high stacking fault energy and more continuous dynamic recrystallization. The FeCoCrNiMnAl0.5 cladding layer formed a slab texture perpendicular to the compression direction, and this cladding layer with a face-centered cubic (FCC) structure had low stacking fault energy, which formed deformed grains that stored many dislocations. The FeCoCrNiMnAl0.5 cladding layer reduced the energy of the FeCoCrNiMnAl cladding layer by storing dislocations, and its cracking tendency during high temperature compression was decreased, thereby extending the service life of the coating surface.

Automated summary

In this study, a gradient high-entropy alloy coating was fabricated by laser cladding, showing excellent balance between strength and toughness and reducing cracking tendency during high temperature compression, thus extending the service life of the coating surface.