期刊
SCRIPTA MATERIALIA
卷 197, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.scriptamat.2021.113814
关键词
Austenitic steels; Oxidation; Corrosion; TEM; TKD
类别
资金
- National Key Research and Development Program of China [YS2018YFE010246]
- Fundamental Research Project of State Key Laboratory of Traction Power [TPL2013]
- EPSRC [EP/K040375/1, EP/N010868/1, EP/R009392/1]
The study found that 19Cr alloy and 25Cr alloy undergo internal oxidation and external oxidation, respectively, after exposure in supercritical water. The higher Cr content in 25Cr alloy leads to the formation of a thinner protective Cr2O3 layer, effectively protecting the sub-surface from further oxidation.
The surface oxide structures formed on two austenitic alloys after exposure in supercritical water were investigated via high-resolution characterization techniques. Results show that the corrosion processes of 19-Cr and 25-Cr alloys are internal oxidation and external oxidation, respectively. 19-Cr alloy shows a typical duplex thick oxide structure, while 25-Cr alloy has a much thinner protective oxide layer mainly composed of Cr2O3. The higher Cr content of 25-Cr alloy exceeds a critical value that enables the conversion from internal to external oxidation, thus facilitates the formation of a thin continuous Cr2O3 layer and protects the sub-surface from further oxidation. (C) 2021 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.