REACTION KINETICS MECHANISMS AND CATALYSIS
卷 133, 期 1, 页码 531-539出版社
SPRINGER
DOI: 10.1007/s11144-021-01971-4
关键词
Photocatalytic degradation; Sol– gel; TiO2; HZSM-5; Acid Red 1
TiO2 nano-crystals were synthesized on HZSM-5 zeolite to facilitate photocatalyst-water separation. The distinct boundaries of TiO2 layer and zeolite demonstrated strong combination. The supported TOHZ photocatalyst showed promising activity on Acid Red 1 degradation, with 45.4% of AR1 molecules degraded after 30 minutes. Reusability test indicated retention of 73.7% activity after five treatment cycles.
The TiO2 nano-crystals were synthesized on the HZSM-5 zeolite to facilitate the photocatalyst-water separation. The HZSM-5 surface was tightly coated with a TiO2 layer in the thickness of approximately 100 nm. The distinct boundaries of the TiO2 layer and the zeolite demonstrated the strong combination of the two materials. There was insignificant effect of this interaction on the properties of the TiO2-HZSM-5 (TOHZ) at a given titanium oxide content. The chemical environments of the two elements in the titanium dioxide were not influenced by the HZSM-5. The E-CB (conduction band edge) and the E-VB (valence band edge) were - 0.63 and 2.45 V for the TOHZ. The supported TOHZ photocatalyst had a promising activity on Acid Red 1 (AR1) degradation. 45.4% of the AR1 molecules were degraded in the solution using 300 mg/L of TOHZ after 30 min of reaction. Reusability test showed that 73.7% of the TOHZ's activity was retained after five treatment cycles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据