JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
卷 72, 期 -, 页码 162-171出版社
JOURNAL MATER SCI TECHNOL
DOI: 10.1016/j.jmst.2020.09.024
关键词
Arrhenius constitution equation; Activation energy map; Hot deformation; Dynamicrecrystallization
资金
- National Natural Science Foundation of China [52034004, 51975404]
The hot deformation behaviors of Ni18Cr9Co9Fe5Nb3Mo superalloy were studied, including activation energy and microstructural features. It was found that the increase in activation energy promotes dynamic recrystallization in the Ni-based superalloy samples.
The hot deformation behaviors of Ni18Cr9Co9Fe5Nb3Mo superalloy were explored in the formation temperature range free of gamma' phase with various strain rates applied. The hot deformation behaviors are initially modeled with Arrhenius equation which gives an average activation energy of 581.1 kJ mol(-1). A modified Arrhenius approach, including the updated Zener-Hollomon parameter is proposed to consider the change of activation energy under different deformation conditions which turns out a relatively accurate computation for activation energy of hot deformation, i.e., the standard variance for modified model calculated in the covered deformation condition is just 35.4 % of that for Arrhenius equation. The modified model also proposes a map for activation energy which ranges from 571.5-589.0 kJ mol(-1) for various deformation conditions. Microstructural features of the representative superalloy specimens were characterized by electron backscattered diffraction (EBSD) techniques in order to clarify the influence of activation energy on the microstructural formation. It is found that the Ni-based superalloy samples with higher activation energy are promoted by the degree of dynamic recrystallization which suggests that the rise in activation energy gives either a better recrystallization rate or finer grains. (C) 2021 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据