期刊
JOURNAL OF HAZARDOUS MATERIALS
卷 410, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jhazmat.2020.124594
关键词
Carbon nitride; Nitrogen defects; One-step synthesis; Photocatalytic H2 evolution
资金
- National Natural Science Foundation of China [22072100]
- NSAF of China [U1730114]
- Open Project of State Key Laboratory of Environment-friendly Energy Materials [18kfhg09]
- Fundamental Research Funds for the Central Universities [20826041D4117]
The ability to manipulate nitrogen defects in carbon nitride by adjusting the heating rate or prolonging the pyrolysis time has been shown to enhance the photocatalytic hydrogen production rate. This method of control results in a higher efficiency compared to conventional methods of CN preparation.
Defects are significant for graphitic carbon nitride (g-C3N4, CN) in photocatalytic applications. Defective CN not only accelerate charge separation but also extend spectral response. Engineering carbon or nitrogen defects in CN has been achieved by variety of strategies, but it is still a long-term interest to develop a simple and controllable route for engineering defects in CN. Herein, we present tuning the nitrogen defects in CN by either changing the heating rate or prolonging the pyrolysis time during polymerization melamine sulfate. It was found that either lower heating rate or longer pyrolysis time lead to the formation of more N vacancies and suspended terminal amino. As a result, an optimal photocatalytic H2 yield rate (? > 420 nm) of 905 ?mol g-1 h-1 was reached, which was 2 times higher than that of CN prepared with a heating rate of 1 ?C/min and pyrolysis at 600 ?C for 4 h.