期刊
CERAMICS INTERNATIONAL
卷 47, 期 14, 页码 20717-20724出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2021.03.335
关键词
Cu2ZnSnS4; Chalcogenide; Electrode; Energy storage; Lithium battery
资金
- UKM Modal Insan [MI-2020-009]
- UKM Research University Grant [GUP201973]
This study synthesized Cu2ZnSnS4 (CZTS) and prepared CZTS/Super P (R) active carbon electrodes, with a discharge capacity superior to other compositions, attributed to favorable pore size for charge carrier transport.
This study aims to identify an optimum electrode composition ratio of Cu2ZnSnS4 (CZTS)/Super P (R) active carbon and evaluate the effects on electrochemical properties of CZTS/Super P (R) electrode in a lithium battery. Hence, the CZTS at a molar ratio of 2:1:1:4 was synthesized using the acetate route sol-gel process which was subsequently annealed at 550 degrees C using argon gas. The copper-rich CZTS stannite structure was confirmed by X-ray diffractometer (XRD) (2 theta = 28.5 degrees, 47.2 degrees and 56.2 degrees), Raman shift (at 283 and 333 cm(-1)) and energy dispersive spectroscopy (EDX) (CZTS-86 = Cu2.6Zn1.2Sn1.5S4 & CZTS-90 = Cu2.2Zn1.2Sn1.2S4) analyses. The CZTS powder produced was then mixed with the polyvinylidene fluoride (PVdF) solution, and Super P (R) to form a homogenous slurry. The slurry was then used to coat a copper substrate before drying in a vacuum oven. Next, the coin cell fabrication process was performed using the prepared CZTS electrode, lithium metal and LiPF6 as an electrolyte. The battery performance analysis upon optimization indicated that the CZTS-86 electrode with open-circuit voltage (OCV) at 1.96 V exhibited a discharge capacity of similar to 571.4 mAh/g. The desired discharge capacity was obtained due to a sufficient pore size of 0.9089 m(2)/g, which provided a favorable condition for charge carrier transport in electrolyte-electrode interfaces. The formation of solid electrolyte interfaces was assumed to have improved electrical characteristics by narrowing the gap created by the high porosities on the electrode surface. This effect can be observed through the reduction of R-ct with an increasing amount of Super P (R). Moreover, the R-ct of the CZTS-86 electrode became consistant after aging compared to other compositions. The improvement of relaxation time (tau) of charge carrier demonstrated a more consistent pattern for Li+ Warburg diffusion coefficient. The electrochemical performances were ascribed to the synergetic effects of different components that make the CZTS electrode a promising electrode material for lithium rechargeable batteries.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据