In this study, efficient sky-blue PeLEDs were fabricated using DJ phase perovskites, with organic diamine cations and RbBr incorporated to increase charge utilization, enhancing radiative recombination through synergistic confinement and passivation effects. The photoluminescence quantum yield approached 70%, and the fabricated PeLEDs achieved an external quantum efficiency of 8.5% with an emission peak at 490 nm.
Two-dimensional Ruddlesden-Popper (RP) and Dion-Jacobson (DJ) phase perovskites are promising alternatives to fabricate blue perovskite light-emitting diodes (PeLEDs) due to their strong quantum/dielectric confinement. While the RP phase perovskites have been widely used as emitter layers in blue PeLEDs, the DJ phase perovskites, possessing better structural stability and charge transfer property, have received little attention. Here, we report the use of DJ phase perovskites for fabricating efficient sky-blue PeLEDs. Organic diamine propane-1,3-diammonium cations were first incorporated into CsPbBr3 to prepare DJ phase perovskites. RbBr was further incorporated as a passivation agent to eliminate traps. It is found that diamine cations and RbBr are interdependent in terms of increasing the utilization of charges. Radiative recombination was enhanced, effectively benefiting from the synergetic confinement and passivation effects. The photoluminescence quantum yield approached 70%. Finally, the fabricated PeLEDs achieved an external quantum efficiency of 8.5% with an emission peak at 490 nm.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据