Characterization of Thin Chromium Coatings Produced by PVD Sputtering for Optical Applications

PVD (physical vapor deposition) and CVD (chemical vapor deposition) have gained greater significance in the last two decades with the mandatory shift from electrodeposition processes to clean deposition processes due to environmental, public safety, and health concerns. Due to the frequent use of coatings in several industrial sectors, the importance of studying the chromium coating processes through PVD-sputtering can be realized, investing in a real alternative to electroplated hexavalent chromium, usually denominated by chromium 6, regularly applied in electrodeposition processes of optical products in the automotive industry. At an early stage, experimental tests were carried out to understand which parameters are most suitable for obtaining chromium coatings with optical properties. To study the coating in a broad way, thickness and roughness analysis of the coatings obtained using SEM and AFM, adhesion analyzes with the scratch-test and transmittance by spectrophotometry were carried out. It was possible to determine that the roughness and transmittance decreased with the increase in the number of layers, the thickness of the coating increased linearly, and the adhesion and resistance to climatic tests remained positive throughout the study. Thus, this study allows for the understanding that thin multilayered Cr coatings can be applied successfully to polymeric substrates regarding optical applications in the automotive industry.

Automated summary

PVD and CVD have become more significant in the past two decades due to concerns about environment, public safety, and health, leading to a shift from electrodeposition to cleaner deposition processes. Studying chromium coating processes through PVD-sputtering is important as an alternative to electroplated hexavalent chromium, especially in the production of optical products in the automotive industry. The study found that thin multilayered Cr coatings can be successfully applied to polymeric substrates for optical applications in the automotive industry.