Experimental and numerical investigation on the thermal and mechanical behaviours of thermal barrier coatings exposed to CMAS corrosion

Calcium-magnesium-alumino-silicate (CMAS) corrosion is a critical factor which causes the failure of thermal barrier coating (TBC). CMAS attack significantly alters the temperature and stress fields in TBC, resulting in their delamination or spallation. In this work, the evolution process of TBC prepared by suspension plasma spraying (SPS) under CMAS attack is investigated. The CMAS corrosion leads to the formation of the reaction layer and subsequent bending of TBC. Based on the observations, a corrosion model is proposed to describe the generation and evolution of the reaction layer and bending of TBC. Then, numerical simulations are performed to investigate the corrosion process of free-standing TBC and the complete TBC system under CMAS attack. The corrosion model constructs a bridge for connecting two numerical models. The results show that the CMAS corrosion has a significant influence on the stress field, such as the peak stress, whereas it has little influence on the steady-state temperature field. The peak of stress increases with holding time, which increases the risk of the rupture of TBC. The Mises stress increases nonlinearly along the thick direction of the reaction layer. Furthermore, in the traditional failure zone, such as the interface of the top coat and bond coat, the stress obviously changes during CMAS corrosion.

Automated summary

Research on the evolution of TBC prepared under CMAS attack reveals that CMAS corrosion leads to the formation of reaction layer and bending of TBC. Numerical simulations show that CMAS corrosion significantly influences the stress field, leading to an increased risk of TBC rupture with increased holding time.