JOURNAL OF NATURAL GAS SCIENCE AND ENGINEERING
卷 86, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jngse.2020.103734
关键词
CO2-H2S corrosion; Failure analysis; Residual corrosion life; Materials selection; Gas well
资金
- National Natural Science Foundation of China [51774249]
- Youth science & technology foundation of SSihuan Province [21CQN0066]
This paper analyzed the failure of gas wells in Northwest Oilfield and provided corresponding solutions. Through experimental methods, it was found that suitable materials should be selected based on depth to prevent corrosion issues.
This paper analyzed the failure of gas wells in Northwest Oilfield and provided corresponding methods to solve the issue. In order to thoroughly investigated the failure factors, methods used in the experiment were material performance testing, SEM, EDS and XRD. Besides, a self-designed HTHP autoclave was used to simulate the real corrosion environment and thereby a new method to choose suitable materials was proposed. The experimental results showed that the chemical composition, metallographic structure, hardness, microstructure and non-metallic inclusion of the failed tubing were all qualified. As a matter of fact, the failure was caused by water-accumulation corrosion which occurred at 6447 m at the bottom of the wellbore, and by water-carrying corrosion occurred at 5086.4m. This paper concluded that the P110ss steel should be selected as tubing in the failed well at a depth of 5086.4m and nickel base alloy steel should be selected at 6447m.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据