卷 65, 期 6, 页码 1211-1216出版社
SPRINGER HEIDELBERG
DOI: 10.1007/s40194-021-01094-3
关键词
Graphite; Aluminum alloy; Active brazing; Interaction
资金
- National Key R&D Program of China [2017YFB0305702]
The study developed an Al-Cu-Si-Ni-Mg brazing filler metal for joining 6063 aluminum alloy and graphite metallized with Ag-Cu-Ti paste. Results showed that joints of good quality can be produced at a brazing temperature of 550°C for 10 minutes, with an average shear strength of 21 MPa. The bonding area mainly consists of various phases including alpha-Al, Ag rich phase, alpha + Al2Cu + Si, Al2Cu, and TiC.
In the present work, an Al-Cu-Si-Ni-Mg brazing filler metal was developed for the joining of 6063 aluminum alloy and graphite metallized with Ag-Cu-Ti paste. The joint microstructures were studied by means of SEM and EDS. Results show that joints with a good quality can be produced at a brazing temperature of 550 degrees C for 10 min. TiC was formed at the graphite/active Ag-Cu-Ti paste interface due to the reaction between Ti and C, and thus, the wettability on the graphite was improved. Compared to the metallization stage, more diffusions of Al, Ag, Ti, and Cu from interlayer to graphite are observed. The bonding area mainly consists of alpha-Al, Ag rich phase, alpha + Al2Cu + Si, Al2Cu, and TiC. It is shown that joints with good quality can be produced and the average shear strength of the joints is 21 MPa.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据