Thermoluminescence glow curve analysis and evaluation of trapping parameters of dysprosium doped lanthanum calcium borate La2CaB10O19

出版社

ELSEVIER
DOI: 10.1016/j.nimb.2020.12.023

关键词

La2CaB10O19; Dy; Thermoluminescence; Trap parameters; Heating rate

向作者/读者索取更多资源

The study focused on thermoluminescence behavior of Dy activated lanthanum calcium borate phosphors, revealing linear TL response and determining the range of activation energy and pre-exponential factor values. It was also observed that heating rate affects the TL behavior, with an anomalous effect observed in Dy3+ doped La2CaB10O19 sample, for which a semi-localized transition model was employed.
The present work elucidates thermoluminescence study of Dy activated lanthanum calcium borate (La2CaB10O19) phosphors and determination of trapping parameters. Two glow curves located at 132 and 295 degrees C were observed and showed a linear TL response. The kinetic parameters of the glow peaks were evaluated using variable heating rate, repeated initial rise method and Computerized Glow Curve Deconvolution. Analysis of the main dosimetric peaks reveals that the values of the activation energy and pre-exponential factor are found to be 0.78-1.145 eV and 8.59 x 10(9)-8.44 x 10(11) s(-1), respectively. The sample doped with 1% Dy3+ exhibits a good stability for the reusability. Besides, the found results indicate that the temperature maximum shifts to the higher temperature side as the heating rate increases. Contrary to previously expressed theoretical expectations, anomalous heating rate dependence was observed in Dy3+ doped La2CaB10O19 sample and a semi-localized transition model explaining the anomalous heating rate effect was employed.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.3
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据