INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS
卷 95, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijrmhm.2020.105442
关键词
Zirconia nanopowders; Densification mechanisms; Pressure effect; Initial stage of sintering
The research showed that increasing the contact area between particles can enhance the compaction effect under different pressures during the sintering process of 3Y-TZP nanopowder, affecting the transition between volume diffusion and grain boundary diffusion.
In order to evaluate the effect of interparticle contact area on the sintering behavior of 3Y-TZP nanopowder, the shrinkage of powder samples, compacted at different pressures were measured under constant rates of heating. Compaction of zirconia NPs at different pressures allowed to increase the contact area between particles and determined the critical parameters when the volume diffusion mechanism is changing on the grain boundary diffusion. It was found that the volume diffusion mechanism is the dominant densification mechanism at the initial stage of sintering for 3Y-TZP nanopowders at a low relative density of green ceramics, when there are few contacting particles, and the grain boundary diffusion mechanism cannot be realized due to the large diffusion path. The domination of the grain boundary diffusion mechanism during initial stage of sintering of 3Y-TZP nanoparticles was detected in case the contact area between particles increased up to 56%.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据