Box-girder; Web cracking; Corrosion; Prestress tensioning technique; Uncertainty
资金
- National Natural Science Foundation of China [52078056]
- Key Project of Hunan Provincial Education Department [18A136]
In this study, a time-dependent prediction model of effective prestress and a corrosion propagation model were established to assess web cracking probability in corroded prestressed concrete bridges. The results showed that the doubled-tensioned prestress technique was more effective in reducing web cracking probability compared to traditional techniques, and epistemic uncertainties significantly impacted the probability of web cracking. Minimizing epistemic uncertainty, especially in chloride diffusion coefficient, is crucial for accurate assessment in this process.
Reasonable assessment of web cracking probability is essential to ensure the service performance of corroded prestressed concrete (PC) bridges. In this paper, a time-dependent prediction model of effective prestress for different prestress tensioning techniques and a corrosion propagation model are established. Meanwhile, an assessment approach of web cracking probability considering both aleatory and epistemic uncertainties is proposed. The case analysis results show that the doubled-tensioned prestress technique is obviously more effective in decreasing the web cracking probability than the traditional prestress tensioning technique. The existing probabilistic method that only considers the aleatory uncertainty may greatly underestimate the probability of web cracking. In comparison, the fastest time to reach the threshold value of web cracking probability when considering the epistemic uncertainty is over 11% earlier than that of using the existing methods. Additionally, the epistemic uncertainty of the chloride diffusion coefficient among the selected corrosion parameters has a most significant impact on the probability of web cracking. Therefore, the epistemic uncertainty of corrosion parameters, especially for the chloride diffusion coefficient, should be minimized as much as possible in this assessment process.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据