Nano mechanical property analysis of single crystal copper using Berkovich nano indenter and molecular dynamic simulation

期刊

COMPUTATIONAL MATERIALS SCIENCE
卷 188, 期 -, 页码 -

出版社

ELSEVIER
DOI: 10.1016/j.commatsci.2020.110237

关键词

Nano indentation; Mechanical property; Molecular dynamics simulation; Crystal orientation; Dislocation

资金

  1. National Natural Science Foundation of China [51865029]

向作者/读者索取更多资源

The molecular dynamics simulation was used to analyze nanoindentation of FCC single crystal copper with different crystal orientations under Berkovich indenter. Crystal orientation significantly influences load distribution, defect formation, slip processes, and dislocation density. Different orientations exhibit variations in hardness and dislocation morphology during indentation.
Nanoindentation analysis of FCC single crystal copper with different crystal orientations under Berkovich indenter was carried out by molecular dynamics simulation. The influence of crystal orientation on load distribution under Berkovich indenter was studied and compared with the experiment. Simultaneously, by establishing the relationship between the load-displacement curve and the instantaneous defect structure, the defect formation and slip processes under different crystal orientations were analyzed. Finally, the dislocation density of different orientations was calculated. Meantime, the relationship between the dislocation density and the hardness was explored. The results show that the < 100 > orientation shows a slightly different anisotropy difference, and the load value is lower than the < 110 > and < 111 > orientations. The < 111 > load value is slightly greater than < 110 > and the hardness values also show the same trend as the load value. The launch time of the initial dislocation loop of < 100 > orientation is earlier than < 110 >, < 111 >. The crystallographic orientation has a great influence on the change of dislocation morphology during the indentation process. With different orientations, the main plastic deformation is incomplete dislocation nucleation. Under different orientations, different forms of dislocation proliferation, such as quadruple, double and triple symmetry, and different stacking slip directions activated during indentation are observed. The < 110 > orientation has a relatively small dislocation density value, the dislocation density rho(0.5) is proportional to the hardness, and the coefficient values are different with different orientations.