卷 191, 期 -, 页码 854-863出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2016.01.148
关键词
Porous carbon sheets; coal tar pitch; MgO template; KOH activation; supercapacitor
资金
- National Natural Science Foundation of China [21406056]
Two-dimensional hierarchical porous carbon sheets (FHPCs) have been prepared by using nano-MgO sheet as template and coal tar pitch as carbon precursor coupled with KOH activation. The weight ratio of pitch with potassium hydroxide (KOH) exerts a marked effect on the porosity of the carbon. The FHPCs materials show some advantages for electrochemical energy storage including a specific surface area of 1454 similar to 1604 m(2) g(-1), sheet structure, hierarchical porosity with macro/meso/micropores, rich O-doping (19 wt%). Resulting from the multiple synergistic effects of these advantages, the FHPC1:2 electrode can achieve a high capacitance of 290 F g(-1) and 250 F g(-1) at 1 A g(-1), 20 A g(-1), respectively, and excellent rate capability with 86% retention rate in 6 M KOH electrolyte. The FHPC1: 2 symmetric supercapacitor displays a high energy density of 20.28 Wh kg(-1) at a power density of 873 W kg(-1) and retains as high as 8.87 Wh kg(-1) at 6389 W kg(-1) in 1 M Na2SO4 electrolyte. Our work demonstrates that KOH activation coupled with flake-like MgO template can act as an excellent route to prepare hierarchical porous carbon sheets from coal tar pitch for high performance supercapacitors. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据