ELECTROCHIMICA ACTA
卷 197, 期 -, 页码 251-262出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2016.02.025
关键词
mesoporous carbon; carbon oxidation; nitrogen doping; ORR; electrocatalysis
资金
- University of Padova [PRAT CPDA139814/13]
- Fuel Cells and Hydrogen Joint Undertaking (FCH-JU) within the CathCat project [303492]
Mesoporous carbons (MCs) are porous materials with high surface area and superior mass transport efficiency than traditional carbon materials that make them attractive to electrocatalytic applications. Doped carbons are particularly interesting due to their possible use as metal-free catalysts for oxygen reduction reaction (ORR) or as electrode support for Pt based catalysts. One of the key points to address for the doped MCs implementation in electrochemical devices, subjected to strong electrochemical stresses, is to determine their durability. In this paper we investigate the chemical modification in nitrogen and sulfur doped or co-doped MCs after ex situ accelerated degradation test (ADT) consisting in ten thousand voltammetric cycles in a potential window of -0.25/+ 1.0 V vs. SCE, in Ar saturated 0.5 M H2SO4, 0.1 M HClO4 or 0.1 M KOH electrolytes. The morphological, chemical and electrochemical properties of doped MCs before and after ADT were evaluated by scanning electron microscopy, thermal gravimetric analysis, Raman and X-ray photoemission spectroscopies, cyclic and linear sweep voltammetries. The carbon materials have proved to keep the porous structure after the ADT, without evident structural collapse. It was found that in acidic and in a lower degree in alkaline electrolytes, pyridinic and pyrrolic functional groups can be oxidized to nitrogen oxide groups, whereas N-graphitic and thiophenic like groups are less affected by the electrochemical oxidation. After ADT, nitrogen doped MCs and, to a lesser extent, sulfur doped MCs resulted to partially lose their catalytic activity towards ORR. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据