Many advantageous properties of cross-linked polymers relate to their network structures. In this study, network structures of three DGEBA-based epoxy systems at various DGEBA monomer sizes were investigated via equilibrium swelling and glass transition behavior. Each system was cured with a tetra-functional diamine, 4,4'-methylenebiscyclohexanamine, in the presence of a nonreactive solvent, i.e., THF at a solvent-to-monomer volume fraction ranging from 0 to 92%. Experimental results revealed that the conventional swelling model (the Dusek model) accurately calculates M-c values of the cured gels prepared in moderate dilute environments, up to approximately 60% by volume of THF. For gels cured in extreme dilute environments, i.e., in the presence of above 60% by volume of THF, the calculated M-c values using the Dusek model were found to increase sharply as a function of the initial solvent content. The observed dramatic increase in M-c values was not supported by the dry T-g of the identical polymer systems. In fact, the dry T-g values of the polymer systems were found to be relatively insensitive to the initial solvent content. A modification was proposed to the Dusek model that incorporates an additional term, which accounts for the probability of finding elastic chains in a polymer network. Using the modified equation, A values were varied as expected with the molecular weight of DGEBA and insensitive to the amount of the solvent initially used during cure. Furthermore, the modified M-c values were shown to be consistent with the dry T-g values in view of the Fox and Loshaek model.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据