Plastic deformation; microstructure; crystallographic orientation; pitting corrosion
资金
- Polish Ministry of Science and Higher Education [DEC-2011/03/B/ST8/05012]
The corrosion behaviour of pure aluminium was studied at the microscale in 0.1M NaCl by combining the electron backscatter diffraction technique and the electrochemical microcell technique. The microstructure was first described. It was found that plastic strain has little influence on these microstructural parameters. After surface preparation, the crystallographic orientation of grains plays a significant role in their corrosion behaviour. Grains oriented along (001) planes are the most resistant to pitting corrosion whereas those oriented along (111) planes are the most susceptible to pitting. After plastic deformation, the susceptibility to pitting corrosion of Al grains is significantly increased and there is no influence of the crystallographic orientation of grains. It was proposed that the presence of a high density of statistically stored dislocations (which cannot be detected by EBSD) affects the physical chemical properties of the oxide film formed on grains. This oxide film degenerates, leading to high susceptibility of pure Al to pitting corrosion. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据