sol-gel; thickness; precursor concentration; SnO2; thin-film transistor
资金
- Basic Science Research Program through the National Research Foundation of Korea (NRF) - Korea government (MSIT) [2019R1F 1A1059788]
Sol-gel processed SnO2 thin-film transistors on SiO2/p(+) Si substrates showed thickness and roughness variations influenced by precursor concentration. Optimized 0.030 M precursor resulted in enhanced device performance with specific mobility of 9.38 cm(2)/Vs and positive threshold voltage of 9.83 V.
Sol-gel processed SnO2 thin-film transistors (TFTs) were fabricated on SiO2/p(+) Si substrates. The SnO2 active channel layer was deposited by the sol-gel spin coating method. Precursor concentration influenced the film thickness and surface roughness. As the concentration of the precursor was increased, the deposited films were thicker and smoother. The device performance was influenced by the thickness and roughness of the SnO2 active channel layer. Decreased precursor concentration resulted in a fabricated device with lower field-effect mobility, larger subthreshold swing (SS), and increased threshold voltage (V-th), originating from the lower free carrier concentration and increase in trap sites. The fabricated SnO2 TFTs, with an optimized 0.030 M precursor, had a field-effect mobility of 9.38 cm(2)/Vs, an SS of 1.99, an I-on/I-off value of similar to 4.0 x 10(7), and showed enhancement mode operation and positive V-th, equal to 9.83 V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据