DOI: 10.3390/coatings10121164
关键词
sandblasting pretreatment; electrodeposition; Ni-Co coating; superhydrophobic; corrosion resistance
资金
- Fundamental Research Funds for the Central Universities [KYXJ202002]
- Jiangsu Agricultural Science and Technology Innovation Fund [CX (20) 3085]
To enhance the corrosion resistance of type C45E4 substrates, a superhydrophobic Ni-Co coating was prepared on a C45E4 surface by sandblasting pretreatment and electrodeposition. The surface microstructure, three-dimensional surface roughness, and crystal structure of the coating was characterized by scanning electron microscope, laser scanning confocal microscope, and X-ray diffraction. An optical surface contact angle measuring instrument and an electrochemical workstation was used to characterize the wettability and corrosion resistance of the surface. The results showed that the water contact angle reached 151.2 degrees on the Ni-Co coating surface. The surface was superhydrophobic and still had stable hydrophobicity after four months. In electrochemical corrosion experiments. Compared with polishing pretreatment, the corrosion current density of superhydrophobic Ni-Co coating prepared by sandblasting pretreatment reached I-corr = 5.05 x 10(-7) A center dot cm(-2), and the corrosion potential reached E-corr = -0.33 V. The superhydrophobic Ni-Co coating had excellent corrosion resistance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据