nanocrystalline alloy; high frequency; magnetic softness; magnetic domain; rapid annealing
资金
- China's State Grid Corporation of Science and Technology Projects [5500-201958390A-0-0-00]
This study found that Mn-doping and rapid annealing in Fe-based nanocrystalline alloys can lead to superior magnetic softness, high-saturation magnetic induction, and large permeability. This is attributed to the superb nano-structural stability and the formation of regular magnetic domains.
Good high-frequency magnetic softness and thermal stability are very important for the wide application of Fe-based nanocrystalline alloys. The present work reports the influence of Mn-doping and rapid annealing on the magnetic softness, nano-structure, and magnetic-microstructure of Fe76-xSi13B8Nb2Cu1Mnx (x = 0, 1, 2, 3, and 4) alloys. It was found that the Fe74Si13B8Nb2Cu1Mn2 alloy exhibits a superior magnetic softness with the high-saturation magnetic induction of 1.32 T and a large permeability at 100 kHz of over 15,000 at a large annealing-temperature region of 120 degrees C. The microstructure and magnetic domains characterization indicate that the good magnetic softness and thermal stabilization can be ascribed to the superb nano-structural stability caused by the Mn doping and rapid annealing at elongated temperatures, which can maintain a fine and high number density alpha-Fe(Si) nano-grains and facilitate the formation of regular and wide domains.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据