Surface Properties of Poly(Hydroxyurethane)s Based on Five-Membered Bis-Cyclic Carbonate of Diglycidyl Ether of Bisphenol A

Poly(hydroxyurethane)s (PHU) are alternatives for conventional polyurethanes due to the use of bis-cyclic dicarbonates and diamines instead of harmful and toxic isocyanates. However, the surface properties of poly(hydroxyurethane)s are not well known. In this work, we focus on the analysis of the surface properties of poly(hydroxyurethane) coatings. Poly(hydroxyurethane)s were obtained by a catalyst-free method from commercially available carbonated diglycidyl ether of bisphenol A (Epidian 6 epoxy resins) and various diamines: ethylenediamine, trimethylenediamine, putrescine, hexamethylenediamine, 2,2,4(2,4,4)-trimethyl-1,6-hexanediamine, m-xylylenediamine, 1,8-diamino-3,6-dioxaoctane, 4,7,10-trioxa-1,13-tridecanediamine, and isophorone diamine, using a non-isocyanate route. The structures of the obtained polymers were confirmed by FT-IR, H-1 NMR and C-13 NMR spectroscopy, and thermogravimetric (TGA) and differential scanning calorimetry (DSC) analyses were performed. The rheological characteristic of the obtained polymers is presented. The static contact angles of water, diidomethane, and formamide, deposited on PHU coatings, were measured. From the measured contact angles, the surface free energy was calculated using two different approaches: Owens-Wendt and van Oss-Chaudhury-Good. Moreover, the wetting envelopes of PHU coatings were plotted, which enables the prediction of the wetting effect of various solvents. The results show that in the investigated coatings, a mainly dispersive interaction occurs.