MATERIALS CHEMISTRY AND PHYSICS
卷 256, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2020.123653
关键词
SiO2/Al2O3; Sapphirine; Dielectric property; Electrical resistivity
资金
- National Natural Science Foundation of China [51764044]
- Natural Science Foundation of Inner Mongolia Autonomous Region [2018LH05021]
- Inner Mongolia Science & Technology Plan [KCBJ2018077]
Glass-ceramics of the MgO-Al2O3-SiO2 (MAS) ternary system were successfully prepared through a melting method with borax, quartz sand, and chemical reagents as the main raw materials. The effects of SiO2/Al2O3 ratios on the structure and properties of glass-ceramics were systematically investigated by differential thermal analysis (DSC), X-ray diffraction (XRD), scanning electron microscope (SEM), dielectric properties and electrical resistivity measurements. The results show that the average coefficient of thermal expansion (CTE) (30-800 degrees C) of all the samples increased with increasing of the SiO2/Al2O3 ratio, but the density of the glass-ceramics and the grain refinement decreased at the same time. The crystalline phase of all the samples was a prepared sapphirine phase when the SiO2/Al2O3 ratio was equal or greater than 1.78 and a second phase of enstatite precipitation. The electrical performance was the best when the SiO2/Al2O3 ratio was equal to 1.27, and its dielectric constant, dielectric loss, and electrical resistivity (room temperature) were 8.78 (1 MHz), 3.55 x 10(-3) (1 MHz), and 10.57 x 10(11) Omega m, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据