Multiscale in-vitro analysis of photo-activated riboflavin incorporated in an experimental universal adhesive

Objective: To investigate the effect of blue light photoactivated riboflavin modified universal adhesives on dentin collagen biodegradation resistance, dentin apparent elastic modulus, and resin-dentin bond strength with interfacial morphology. Methods: Dentin slabs were treated with 0.1% riboflavin-5-phosphate modified (powder added slowly while shaking and then sonicated to enhance the dispersion process) Universal Adhesive Scotch Bond and ZipbondTM along with control (non-modified) and experimental adhesives, photoactivated with blue light for 20s. Hy-droxyproline (HYP) release was assessed after 1-week storage. Elastic-modulus testing was evaluated using universal testing machine at 24 h. Resin-dentin interfacial morphology was assessed with scanning electron microscope, after 6-month storage. 0.1% rhodamine dye was added into each adhesive and analyzed using CLSM. Detection of free amino groups was carried out using ninhydrin and considered directly proportional to optical absorbance. Collagen molecular confirmation was determined using spectropolarimeter to evaluate and assess CD spectra. For molecular docking studies with riboflavin (PDB ID file), the binding pocket was selected with larger SiteScore and DScore using Schrodinger PB software. After curing, Raman shifts in Amide regions were obtained at 8 mu m levels. Data were analyzed using Two-way analysis of variance (ANOVA, p <= 0.05) and Tukey-Kramer multiple comparison post hoc tests. Results: At baseline, bond strength reduced significantly (p <= 0.05) in control specimens. However, at 6 months' storage, UVA ZipbondTM had significantly higher mu TBS. Resin was able to diffuse through the porous demineralized dentin creating adequate hybrid layers in both 0.1%RF modified adhesives in CLSM images. In riboflavin groups, hybrid layer and resin tags were more pronounced. The circular dichroism spectrum showed negative peaks for riboflavin adhesive specimens. Best fitted poses adopted by riboflavin compound are docked with MMP-2 and-9 proteases. Amide bands and CH2 peaks followed the trend of being lowest for control UA Scotch bond adhesive specimens and increasing in Amides, proline, and CH2 intensities in 0.1%RF modified adhesive specimens. All 0.1%RF application groups showed statistically significant (p < 0.05) less levels of HYP released compared to controls. Dentin Eappr of riboflavin application was significantly (p < 0.05) more as compared to control groups. Conclusion: Blue light photoactivated 0.1% riboflavin modified adhesives improved the biochemical and biomechanical properties of demineralized dentin as well as the long-term resin-dentin interfacial integrity and bond strength of universal adhesive to dentin.